Precalentamiento M270M Gr.345W — H16, Mid HI, > 60 mm: 375°F

M270M Gr.345W / M270 Gr.50W

AASHTO M270M Gr.345W (M270 Gr.50W) is a weathering bridge steel with 345 MPa (50 ksi) yield that forms a protective oxide patina for unpainted bridge service. The copper-chromium-nickel alloying provides atmospheric corrosion resistance, eliminating lifetime repainting costs estimated at $15–25 per square foot per cycle. Weld filler must match the weathering composition (E8018-W2 or equivalent) for exposed joints. NFC preheat per Table 6.3 Group 1; FC per Tables 12.6/12.7 which carry higher preheat than the non-weathering grades.

Entendiendo el Precalentamiento FC para M270M Gr.345W / M270 Gr.50W

Weathering 345 MPa (50 ksi) bridge steel for unpainted service. Under D1.5 fracture-critical requirements (Clause 12), the combination of H16 hydrogen designation and this heat input band requires 375°F minimum preheat at > 60 mm (> 2½ in). Lower hydrogen levels (H4 < H8 < H16) allow lower preheat because less hydrogen enters the weld deposit. Similarly, higher heat input reduces preheat requirements because slower cooling rates give hydrogen more time to diffuse out.

Dónde se Usa M270M Gr.345W / M270 Gr.50W

Deployed in unpainted bridge plate girders across humid, coastal, and high-maintenance-cost environments. The weathering patina eliminates lifetime repainting cycles estimated at $15–25/sq ft per cycle. Weld filler must match the weathering composition (E8018-W2 or ER80S-G-W) for exposed joints to ensure the weld face develops the same protective oxide as the base metal. Conventional Gr.345W is being replaced by HPS345W in new designs due to superior weldability.

Control de Hidrógeno H16 para M270M Gr.345W / M270 Gr.50W

Weathering Gr.345W (50W) at H16 is used for field splices when self-shielded FCAW is the only practical process due to wind exposure on elevated bridge erection. The significantly higher preheat at H16 — often 40–60°F above H4 — makes weather-window scheduling critical for winter field splice operations.

Por qué el Precalentamiento Importa en > 60 mm (> 2½ in)

Material over 65 mm (2-1/2 in) includes the heaviest bridge girder flanges and box-section walls. Table 6.3 requires 110°C (225°F) for both groups at this thickness. Extended preheat soak time is necessary to achieve uniform through-thickness temperature. FC preheat for the heaviest sections reaches 180–200°C (350–400°F) at the H16 hydrogen level.

M270M Gr.345W / M270 Gr.50W en > 60 mm (> 2½ in)

Gr.345W (50W) above 65 mm is increasingly rare as HPS345W replaces it in new designs. The conventional weathering composition at this thickness has elevated lamellar tearing risk from sulfide inclusion elongation — the problem that drove development of the HPS grades with calcium-treated, inclusion-shape-controlled steel. Existing bridges with thick 345W flanges require careful Z-direction tension checks during rehabilitation welding.

Mayor Precalentamiento con Designación H16

Los consumibles H16 permiten hasta 16 mL de hidrógeno difusible por 100g — el nivel más alto permitido para soldadura FC de puentes. En > 60 mm (> 2½ in) con aporte térmico 2.0–2.8 kJ/mm, el precalentamiento de 375°F (190°C) compensa el mayor potencial de hidrógeno.

Otros Aceros de Puente en H16 2.0–2.8 kJ/mm · > 60 mm (> 2½ in)

M270M Gr.345W / M270 Gr.50W en H16 2.0–2.8 kJ/mm

Prueba Diferentes Combinaciones