Pré-aquecimento M270M HPS345W — H8, Mid HI, > 60 mm: 350°F

M270M HPS345W / M270 HPS50W

AASHTO M270M HPS345W (M270 HPS50W) is a high-performance weathering bridge steel with enhanced weldability through controlled chemistry — 0.11% max carbon, 0.006% max sulfur with calcium treatment for inclusion shape control. Developed under FHWA-funded research to eliminate the lamellar tearing and inconsistent toughness problems of earlier weathering steel bridge designs. The lower carbon equivalent compared to conventional Gr.345W reduces cracking sensitivity at flange splices. NFC preheat per Table 6.3 Group 1; FC per Tables 12.6/12.7.

Entendendo o Pré-aquecimento FC para M270M HPS345W / M270 HPS50W

High-performance weathering 345 MPa steel with enhanced weldability. Under D1.5 fracture-critical requirements (Clause 12), the combination of H8 hydrogen designation and this heat input band requires 350°F minimum preheat at > 60 mm (> 2½ in). Lower hydrogen levels (H4 < H8 < H16) allow lower preheat because less hydrogen enters the weld deposit. Similarly, higher heat input reduces preheat requirements because slower cooling rates give hydrogen more time to diffuse out.

Onde M270M HPS345W / M270 HPS50W é Usado

Preferred over conventional Gr.345W for new unpainted bridge construction. The HPS designation indicates FHWA-developed chemistry with 0.11% max carbon and controlled sulfur for enhanced weldability and lamellar tearing resistance. Flange splice CJP welds benefit from the lower carbon equivalent, reducing reject rates during cold-weather bridge fabrication. Material cost premium over standard Gr.345W is typically 15–25% per ton but eliminates weldability-related rework.

Controle de Hidrogênio H8 para M270M HPS345W / M270 HPS50W

HPS345W (HPS50W) with H8 is common practice where the HPS weldability advantage partially compensates for the higher hydrogen level. The controlled chemistry means HPS345W at H8 often has lower total cracking susceptibility than conventional 345W at H4 — illustrating how base metal chemistry and hydrogen control interact.

Por que o Pré-aquecimento Importa em > 60 mm (> 2½ in)

Material over 65 mm (2-1/2 in) includes the heaviest bridge girder flanges and box-section walls. Table 6.3 requires 110°C (225°F) for both groups at this thickness. Extended preheat soak time is necessary to achieve uniform through-thickness temperature. FC preheat for the heaviest sections reaches 180–200°C (350–400°F) at the H16 hydrogen level.

M270M HPS345W / M270 HPS50W em > 60 mm (> 2½ in)

HPS345W (HPS50W) above 65 mm is the preferred material for heavy unpainted bridge flanges replacing conventional 345W. The sulfur control (0.006% max) and calcium treatment ensure clean steel with minimal through-thickness anisotropy. At this thickness, the weldability advantage is most pronounced — conventional 345W at 65+ mm required expensive preheat and post-weld hydrogen bake-out procedures that HPS chemistry largely eliminates.

Outros Aços de Ponte em H8 2.0–2.8 kJ/mm · > 60 mm (> 2½ in)

M270M HPS345W / M270 HPS50W em H8 2.0–2.8 kJ/mm

Experimente Diferentes Combinações

Use a Calculadora de Pré-aquecimento D1.5 para Pontes para consultar qualquer aço AASHTO M270, nível de hidrogênio e combinação de aporte de calor. Veja também a Calculadora de Pré-aquecimento D1.1 para aço estrutural.