Pré-aquecimento M270M Gr.250 — H4, High HI, > 60 mm: 250°F

M270M Gr.250 / M270 Gr.36

AASHTO M270M Gr.250 (M270 Gr.36) is the metric/US customary designation for the basic structural bridge steel with 250 MPa (36 ksi) minimum yield. It is the direct bridge equivalent of ASTM A709 Gr.36, procured under AASHTO M270 with mandatory Charpy V-notch testing per temperature zone. Used for secondary bridge members — lateral bracing, diaphragm plates, floor beam stiffeners, and bearing components where Gr.345 strength is not needed. Non-fracture-critical preheat follows Table 6.3 Group 1; fracture-critical follows Tables 12.4/12.5 with hydrogen and heat input as additional variables.

Entendendo o Pré-aquecimento FC para M270M Gr.250 / M270 Gr.36

Basic 250 MPa (36 ksi) bridge steel for secondary members. Under D1.5 fracture-critical requirements (Clause 12), the combination of H4 hydrogen designation and this heat input band requires 250°F minimum preheat at > 60 mm (> 2½ in). Lower hydrogen levels (H4 < H8 < H16) allow lower preheat because less hydrogen enters the weld deposit. Similarly, higher heat input reduces preheat requirements because slower cooling rates give hydrogen more time to diffuse out.

Onde M270M Gr.250 / M270 Gr.36 é Usado

Specified for secondary bridge members under AASHTO LRFD — lateral bracing angles, diaphragm plates, floor beam stiffeners, bearing seat components, and railing posts. Gr.250 (36) requires CVN testing per AASHTO temperature zone, distinguishing it from plain ASTM A36 by guaranteeing fracture resistance at the bridge design service temperature. Transverse stiffener fillet welds and floor beam web-to-flange joints are high-frequency fabrication details. Temperature zones (1 through 3) determine CVN test temperature: Zone 1 at 21°C (70°F) for moderate climates, Zone 2 at 4°C (40°F) for cold, Zone 3 at -12°C (10°F) for severe cold.

Controle de Hidrogênio H4 para M270M Gr.250 / M270 Gr.36

For Gr.250 (36), the H4 restriction to 4 mL/100g diffusible hydrogen provides the widest margin against cold cracking in secondary bridge members. The low carbon equivalent of Gr.250 already makes it one of the least crack-sensitive bridge steels, so the practical benefit of H4 over H8 is primarily preheat reduction — often 10–20°C (20–40°F) lower, which speeds production on high-volume stiffener and bracing fabrication.

Por que o Pré-aquecimento Importa em > 60 mm (> 2½ in)

Material over 65 mm (2-1/2 in) includes the heaviest bridge girder flanges and box-section walls. Table 6.3 requires 110°C (225°F) for both groups at this thickness. Extended preheat soak time is necessary to achieve uniform through-thickness temperature. FC preheat for the heaviest sections reaches 180–200°C (350–400°F) at the H16 hydrogen level.

M270M Gr.250 / M270 Gr.36 em > 60 mm (> 2½ in)

Gr.250 (36) above 65 mm is rare — typically only in large bearing assemblies or rehabilitation projects repairing older bridges where original plate was overspecified. Preheat soak-through at 225°F requires flame heating on both sides for 15–20 minutes on plate this thick. The cost of preheat compliance at this thickness often triggers a design review to consider switching to Gr.345 which achieves the same capacity with thinner, lighter sections.

Consumíveis Certificados H4 para Soldagem FC de Pontes

O designador suplementar H4 certifica que o consumível deposita no máximo 4 mL de hidrogênio difusível por 100g de metal depositado. Para fratura crítica M270M Gr.250 / M270 Gr.36 em espessura > 60 mm (> 2½ in) com aporte de calor > 2.8 kJ/mm, os consumíveis H4 alcançam o menor pré-aquecimento de 250°F (120°C) nas tabelas FC.

Outros Aços de Ponte em H4 > 2.8 kJ/mm · > 60 mm (> 2½ in)

M270M Gr.250 / M270 Gr.36 em H4 > 2.8 kJ/mm

Experimente Diferentes Combinações

Use a Calculadora de Pré-aquecimento D1.5 para Pontes para consultar qualquer aço AASHTO M270, nível de hidrogênio e combinação de aporte de calor. Veja também a Calculadora de Pré-aquecimento D1.1 para aço estrutural.

Guias Relacionados