예열 M270M Gr.345W — H16, Mid HI, 40–60 mm: 325°F

M270M Gr.345W / M270 Gr.50W

AASHTO M270M Gr.345W (M270 Gr.50W) is a weathering bridge steel with 345 MPa (50 ksi) yield that forms a protective oxide patina for unpainted bridge service. The copper-chromium-nickel alloying provides atmospheric corrosion resistance, eliminating lifetime repainting costs estimated at $15–25 per square foot per cycle. Weld filler must match the weathering composition (E8018-W2 or equivalent) for exposed joints. NFC preheat per Table 6.3 Group 1; FC per Tables 12.6/12.7 which carry higher preheat than the non-weathering grades.

M270M Gr.345W / M270 Gr.50W의 FC 예열 이해

Weathering 345 MPa (50 ksi) bridge steel for unpainted service. Under D1.5 fracture-critical requirements (Clause 12), the combination of H16 hydrogen designation and this heat input band requires 325°F minimum preheat at 40–60 mm (1½–2½ in). Lower hydrogen levels (H4 < H8 < H16) allow lower preheat because less hydrogen enters the weld deposit. Similarly, higher heat input reduces preheat requirements because slower cooling rates give hydrogen more time to diffuse out.

M270M Gr.345W / M270 Gr.50W이 사용되는 곳

Deployed in unpainted bridge plate girders across humid, coastal, and high-maintenance-cost environments. The weathering patina eliminates lifetime repainting cycles estimated at $15–25/sq ft per cycle. Weld filler must match the weathering composition (E8018-W2 or ER80S-G-W) for exposed joints to ensure the weld face develops the same protective oxide as the base metal. Conventional Gr.345W is being replaced by HPS345W in new designs due to superior weldability.

M270M Gr.345W / M270 Gr.50W의 H16 수소 제어

Weathering Gr.345W (50W) at H16 is used for field splices when self-shielded FCAW is the only practical process due to wind exposure on elevated bridge erection. The significantly higher preheat at H16 — often 40–60°F above H4 — makes weather-window scheduling critical for winter field splice operations.

40–60 mm (1½–2½ in)에서 예열이 중요한 이유

Material from 40 to 65 mm (1-1/2 to 2-1/2 in) covers heavy girder flanges, thick splice plates, and main member plate. This is the critical thickness range for bridge fabrication — preheat reaches 65°C (150°F) for Group 1 and 80°C (175°F) for Group 2. FC preheat at this thickness can exceed 200°C (400°F) depending on hydrogen level and heat input.

40–60 mm (1½–2½ in)에서의 M270M Gr.345W / M270 Gr.50W

Gr.345W (50W) at 40–65 mm covers girder flanges on medium-span unpainted bridges where the lifecycle cost of eliminating repainting outweighs the modest material premium. The higher-alloy chemistry for weathering resistance increases the carbon equivalent compared to plain Gr.345, which is why D1.5 assigns weathering grades to Tables 12.6/12.7 rather than 12.4/12.5 for FC preheat — a separate set of tables with generally higher preheat requirements reflecting the increased cracking susceptibility of the Cu-Cr-Ni alloying elements. Flange splice procedures must account for the weathering composition by matching filler metals to ensure consistent patina development across the weld face.

H16 지정 시 높은 예열

H16 용접재료는 100g당 최대 16 mL의 확산성 수소를 허용합니다 — FC 교량 용접에서 허용되는 가장 높은 수준입니다. 40–60 mm (1½–2½ in)에서 2.0–2.8 kJ/mm 입열량 시 325°F (160°C) 예열은 높은 수소 잠재력을 보상합니다.

H16 2.0–2.8 kJ/mm · 40–60 mm (1½–2½ in)에서의 다른 교량 강재

H16 2.0–2.8 kJ/mm에서의 M270M Gr.345W / M270 Gr.50W

다양한 조합 시도

D1.5 교량 예열 계산기를 사용하여 AASHTO M270 강재, 수소 수준 및 입열량 조합을 조회하세요. D1.1 예열 계산기도 참조하세요.