Preheat M270M HPS345W — H4, High HI, 20–40 mm: 150°F

M270M HPS345W / M270 HPS50W

AASHTO M270M HPS345W (M270 HPS50W) is a high-performance weathering bridge steel with enhanced weldability through controlled chemistry — 0.11% max carbon, 0.006% max sulfur with calcium treatment for inclusion shape control. Developed under FHWA-funded research to eliminate the lamellar tearing and inconsistent toughness problems of earlier weathering steel bridge designs. The lower carbon equivalent compared to conventional Gr.345W reduces cracking sensitivity at flange splices. NFC preheat per Table 6.3 Group 1; FC per Tables 12.6/12.7.

Memahami Preheat FC untuk M270M HPS345W / M270 HPS50W

High-performance weathering 345 MPa steel with enhanced weldability. Under D1.5 fracture-critical requirements (Clause 12), the combination of H4 hydrogen designation and this heat input band requires 150°F minimum preheat at 20–40 mm (3/4–1½ in). Lower hydrogen levels (H4 < H8 < H16) allow lower preheat because less hydrogen enters the weld deposit. Similarly, higher heat input reduces preheat requirements because slower cooling rates give hydrogen more time to diffuse out.

Di Mana M270M HPS345W / M270 HPS50W Digunakan

Preferred over conventional Gr.345W for new unpainted bridge construction. The HPS designation indicates FHWA-developed chemistry with 0.11% max carbon and controlled sulfur for enhanced weldability and lamellar tearing resistance. Flange splice CJP welds benefit from the lower carbon equivalent, reducing reject rates during cold-weather bridge fabrication. Material cost premium over standard Gr.345W is typically 15–25% per ton but eliminates weldability-related rework.

Kontrol Hidrogen H4 untuk M270M HPS345W / M270 HPS50W

HPS345W (HPS50W) already has inherently low carbon equivalent due to HPS chemistry control. Combined with H4 consumables, the preheat requirement drops to the lowest tier in Tables 12.6/12.7 — frequently 20–30°F lower than conventional 345W, compounding the weldability advantage of HPS chemistry with optimized hydrogen control.

Mengapa Preheat Penting pada 20–40 mm (3/4–1½ in)

Material from 20 to 40 mm (3/4 to 1-1/2 in) includes many girder web plates, splice plates, and bearing stiffener plates. Preheat increases to 20°C (70°F) for Group 1 and 50°C (125°F) for Group 2 under Table 6.3. The thicker section slows hydrogen diffusion, requiring higher preheat to maintain safe cooling rates.

M270M HPS345W / M270 HPS50W pada 20–40 mm (3/4–1½ in)

At 20–40 mm, HPS345W (HPS50W) appears in splice plates and web plates for new unpainted bridge construction. The calcium-treated, inclusion-shape-controlled chemistry virtually eliminates lamellar tearing at through-thickness-loaded connections — a critical advantage for corner joints at bearing stiffener-to-flange connections where Z-direction tensile stresses develop during welding contraction.

Bahan Habis Pakai Bersertifikat H4 untuk Pengelasan FC Jembatan

Penunjukan tambahan H4 menyertifikasi bahwa bahan habis pakai mengendapkan tidak lebih dari 4 mL hidrogen difusibel per 100g logam yang diendapkan. Untuk fraktur kritis M270M HPS345W / M270 HPS50W pada ketebalan 20–40 mm (3/4–1½ in) dengan masukan panas > 2.8 kJ/mm, bahan habis pakai H4 mencapai preheat terendah 150°F (70°C) di tabel FC.

Baja Jembatan Lain pada H4 > 2.8 kJ/mm · 20–40 mm (3/4–1½ in)

M270M HPS345W / M270 HPS50W pada H4 > 2.8 kJ/mm

Coba Kombinasi Berbeda

Gunakan Kalkulator Preheat Jembatan D1.5 untuk mencari baja AASHTO M270, tingkat hidrogen, dan kombinasi masukan panas. Lihat juga Kalkulator Preheat D1.1 untuk baja struktural.

Panduan Terkait