Preheat M270M Gr.345 — H8, Mid HI, ≤ 20 mm: 100°F

M270M Gr.345 / M270 Gr.50

AASHTO M270M Gr.345 (M270 Gr.50) is the standard bridge plate and shape grade with 345 MPa (50 ksi) minimum yield, corresponding to ASTM A709 Gr.50. It is the baseline strength for modern highway bridge design per AASHTO LRFD. Used for plate girder flanges, webs, floor beams, cross-frames, and splice plates. Flanges on large plate girders routinely reach 50–75 mm (2–3 in) thick, making preheat compliance at upper thickness tiers a significant production consideration. NFC preheat per Table 6.3 Group 1; FC per Tables 12.4/12.5.

Memahami Preheat FC untuk M270M Gr.345 / M270 Gr.50

Standard 345 MPa (50 ksi) bridge plate for girders and floor beams. Under D1.5 fracture-critical requirements (Clause 12), the combination of H8 hydrogen designation and this heat input band requires 100°F minimum preheat at ≤ 20 mm (3/4 in). Lower hydrogen levels (H4 < H8 < H16) allow lower preheat because less hydrogen enters the weld deposit. Similarly, higher heat input reduces preheat requirements because slower cooling rates give hydrogen more time to diffuse out.

Di Mana M270M Gr.345 / M270 Gr.50 Digunakan

Standard for highway bridge plate girder flanges, box girder webs, cross-frame angles, bearing sole plates, and splice plates in bolted-welded connections. Gr.345 (50) is the baseline strength for modern AASHTO LRFD bridge design. Flange butt splices, web-to-flange continuous fillet welds, and bearing stiffener clips are the dominant weld types in girder fabrication. Girder flanges typically range from 20 to 75 mm (3/4 to 3 in) thick with widths from 300 to 750 mm (12 to 30 in), requiring extended preheat soak times on thicker flange splices.

Kontrol Hidrogen H8 untuk M270M Gr.345 / M270 Gr.50

Gr.345 (50) with H8 is the standard specification for most bridge fabrication shops. H8 consumables are more widely stocked than H4, providing procurement flexibility without significantly increasing preheat requirements. The preheat increase from H4 to H8 is typically 10–25°F depending on thickness tier.

Mengapa Preheat Penting pada ≤ 20 mm (3/4 in)

Material up to 20 mm (3/4 in) covers most cross-frame angles, stiffener clips, lateral bracing members, and light bridge plate. At this thickness, hydrogen diffusion is efficient and preheat requirements are the lowest in Table 6.3 — 10°C (50°F) for both groups. In FC service, this thickness tier also carries the lowest preheat in Tables 12.4–12.7, starting at 40°C (100°F) for H4 consumables.

M270M Gr.345 / M270 Gr.50 pada ≤ 20 mm (3/4 in)

Gr.345 (50) under 20 mm covers web stiffeners, bearing stiffener clips, and cross-frame gusset plates — the highest-volume weld details in girder fabrication. These thin plates are fillet-welded to girder webs using semi-automatic FCAW with E71T-1 wire at 2–4 kg/hr deposition. Preheat is quick to achieve with a rosebud torch and verifiable with a temperature-indicating crayon. Joint fit-up at this thickness is critical because thin plate distortion from uncontrolled heat input causes cumulative girder sweep.

Baja Jembatan Lain pada H8 2.0–2.8 kJ/mm · ≤ 20 mm (3/4 in)

M270M Gr.345 / M270 Gr.50 pada H8 2.0–2.8 kJ/mm

Coba Kombinasi Berbeda

Gunakan Kalkulator Preheat Jembatan D1.5 untuk mencari baja AASHTO M270, tingkat hidrogen, dan kombinasi masukan panas. Lihat juga Kalkulator Preheat D1.1 untuk baja struktural.

Panduan Terkait