A516 Gr.65/70 Preheat for GMAW — 1-1/2" to 2-1/2"

GMAW (Gas Metal Arc Welding)

GMAW (MIG) feeds continuous solid wire with shielding gas — an inherently low-hydrogen process assigned to Category B in Table 5.11.

For pressure vessel work, GMAW with ER70S-6 provides excellent deposition rates on long seam welds. Gas backing with argon on back-purged root passes produces a smooth internal weld profile that satisfies radiographic acceptance criteria. Shielding gas purity is critical for vessel code quality; dew point must be below -40°F.

GMAW Tips for Pressure Vessel and Low-Temperature Steels

For A516 Grades 65/70 pressure vessel plate (35–38 ksi yield), GMAW spray transfer at 260–300 A with 0.045" ER70S-6 delivers 8–12 lb/hr on vessel longitudinal and circumferential seams. Category B only — no non-LH SMAW option. On thick Gr.70 plate, Category B minimum preheat is 150°F [65°C] over 1-1/2 thru 2-1/2 in and 225°F [110°C] over 2-1/2 in. Maintain interpass below 400°F for consistent weld metal properties on multi-pass vessel shell joints.

Typical values for reference — always verify against your approved WPS and electrode manufacturer data.

Filler Metal for GMAW

Common wire: ER70S-6 (AWS A5.18). Diameter: 0.035" for thin sections and out-of-position, 0.045" for production flat/horizontal. Shielding gas: 75/25 Ar/CO2 (standard), 90/10 Ar/CO2 (less spatter, better profile), or 100% CO2 (deeper penetration, more spatter). Contact-tip-to-work distance: 1/2" to 3/4".

Typical values for reference — always verify against your approved WPS and electrode manufacturer data.

A516 Gr.65/70

ASTM A516 Grades 65 and 70 are the higher-strength pressure vessel plates in this specification, with 65 and 70 ksi minimum tensile strength and 35/38 ksi minimum yield respectively. Used in higher-pressure vessels, distillation columns, and reactor shells, they require low-hydrogen welding processes (Category B only in Table 5.11) due to their higher carbon equivalent compared to Grades 55/60. Carbon limits are 0.28% max for Gr.65 and 0.31% max for Gr.70 on thicker plate, pushing the CE-IIW into the 0.43-0.48 range where non-low-hydrogen SMAW is no longer prequalified. A516 Gr.70 is the single most specified plate grade for ASME Section VIII Division 1 pressure vessels, accounting for an estimated 40%+ of all vessel plate orders in North America.

Why This Preheat for A516 Gr.65/70 with GMAW

Higher-strength pressure vessel plate requiring low-hydrogen processes only. This steel is prequalified only with low-hydrogen processes under Table 5.11. With GMAW, the continuous solid wire and gas shielding in GMAW produce inherently low hydrogen levels, typically 2-4 mL/100g. The 150°F minimum preheat balances the steel’s strength level and carbon equivalent against the hydrogen control provided by GMAW. Non-low-hydrogen SMAW is not an option for this grade under D1.1 prequalified WPS.

Typical Applications for A516 Gr.65/70

Used in higher-pressure process vessels, distillation columns, reactor shells, thick-wall accumulators, high-pressure heat exchangers, and flare knockout drums. A516 Gr.70 plate is common in ASME VIII Division 1 vessels above 250 psi design pressure and in columns operating under hydroprocessing conditions. Longitudinal seams on heavy-wall vessels and nozzle-to-shell set-on welds are critical joint configurations requiring strict preheat compliance. Wall thicknesses in high-pressure service can exceed 3" on large-diameter vessels, with shell diameters from 24" to over 15 feet. Post-weld heat treatment per ASME Code is frequently required for A516 Gr.70 above 1-1/4" wall thickness, adding PWHT soak temperature (typically 1100-1200°F) and hold time (1 hour per inch of thickness) to the fabrication sequence. PWHT stress-relieves the weld and HAZ but does not change the preheat requirements during the initial welding operation.

Why Preheat Matters at 1-1/2" to 2-1/2"

Heavy plate with significant restraint and thermal mass — preheat is critical to maintain slow cooling for hydrogen escape.

Other Steels with GMAW at 1-1/2" to 2-1/2"

A516 Gr.65/70 with GMAW

Try Different Combinations

Use the interactive preheat calculator to look up any steel, process, and thickness combination from D1.1:2025 Table 5.11.

A516 Gr.65/70 Welding Guides