A516 Gr.55/60 Preheat for GMAW — over 2-1/2"

GMAW (Gas Metal Arc Welding)

GMAW (MIG) feeds continuous solid wire with shielding gas — an inherently low-hydrogen process assigned to Category B in Table 5.11.

For pressure vessel work, GMAW with ER70S-6 provides excellent deposition rates on long seam welds. Gas backing with argon on back-purged root passes produces a smooth internal weld profile that satisfies radiographic acceptance criteria. Shielding gas purity is critical for vessel code quality; dew point must be below -40°F.

Why GMAW for A516 Gr.55/60 at over 2-1/2"

Why GMAW for A516 Gr.55/60 at over 2-1/2"? GMAW delivers 8-12 lb/hr deposition — compared to <a href="/welding/preheat-calculator/a516-5560/saw/over-2-1-2-inch/">SAW</a> at 15-40 lb/hr. Position capability: all positions (not GMAW-S). Suitability: primarily shop.

Filler Metal for GMAW

Common wire: ER70S-6 (AWS A5.18). Diameter: 0.035" for thin sections and out-of-position, 0.045" for production flat/horizontal. Shielding gas: 75/25 Ar/CO2 (standard), 90/10 Ar/CO2 (less spatter, better profile), or 100% CO2 (deeper penetration, more spatter). Contact-tip-to-work distance: 1/2" to 3/4".

Typical values for reference — always verify against your approved WPS and electrode manufacturer data.

A516 Gr.55/60

ASTM A516 Grades 55 and 60 are carbon steel plates designed for moderate and lower temperature pressure vessel service. Grade 55 (55 ksi tensile, 30 ksi yield) and Grade 60 (60 ksi tensile, 32 ksi yield) are widely used in storage tanks, heat exchangers, and process drums. Chemistry limits (0.24% max carbon for Gr.55, 0.27% max carbon for Gr.60 on thicker plate) and typical carbon equivalent of 0.38-0.44 qualify them for both Category A (non-low-hydrogen) and Category B preheat in Table 5.11. A516 is produced in plate thicknesses from 1/4" through 12". Grades 55 and 60 may be ordered as-rolled, normalized, or stress-relieved depending on the ASME Code requirements for the specific vessel design temperature and thickness.

Why This Preheat for A516 Gr.55/60 with GMAW

Pressure vessel plate for storage tanks and heat exchangers at moderate strength. With low-hydrogen GMAW, this combination falls under Category B rather than Category A — the continuous solid wire and gas shielding in GMAW produce inherently low hydrogen levels, typically 2-4 mL/100g. The 225°F minimum preheat is lower than what non-low-hydrogen SMAW would require at the same thickness because GMAW significantly reduces the driving force for hydrogen-induced cracking in the heat-affected zone.

Typical Applications for A516 Gr.55/60

Specified for atmospheric storage tank shells per API 650, heat exchanger tube sheets, air receiver vessels, condensate drums, deaerator shells, and low-pressure separator vessels. A516 Gr.60 is the workhorse for ASME VIII Division 1 vessels under 650°F design temperature. Shell-to-head circumferential seams and nozzle reinforcement pads are the primary weld details. Plate thicknesses for API 650 tank shells typically range from 5/16" at the top course to 1" or more at the bottom course depending on tank diameter and liquid specific gravity. Vertical seam welds carry the full hydrostatic head and require complete joint penetration with radiographic examination. Tank diameters range from 15 feet for small day tanks to over 300 feet for crude oil terminal storage. Shop-welded vessel shells are rolled from flat plate with longitudinal seams welded first, then circumferential seams joining shell courses together on the vessel rotator.

Why Preheat Matters at over 2-1/2"

The heaviest sections demand the highest preheat in Table 5.11. Multi-pass sequences require maintaining interpass temperature throughout.

Other Steels with GMAW at over 2-1/2"

A516 Gr.55/60 with GMAW

Try Different Combinations

Use the interactive preheat calculator to look up any steel, process, and thickness combination from D1.1:2025 Table 5.11.

A516 Gr.55/60 Welding Guides