M270M Gr.345W Preheat — H8, High HI, 40–60 mm: 275°F
Fracture-critical preheat requirement for M270M Gr.345W / M270 Gr.50W at 40–60 mm (1½–2½ in) thickness with H8 hydrogen designation, per AASHTO/AWS D1.5:2025, the Bridge Welding Code.
M270M Gr.345W / M270 Gr.50W
AASHTO M270M Gr.345W (M270 Gr.50W) is a weathering bridge steel with 345 MPa (50 ksi) yield that forms a protective oxide patina for unpainted bridge service. The copper-chromium-nickel alloying provides atmospheric corrosion resistance, eliminating lifetime repainting costs estimated at $15–25 per square foot per cycle. Weld filler must match the weathering composition (E8018-W2 or equivalent) for exposed joints. NFC preheat per Table 6.3 Group 1; FC per Tables 12.6/12.7 which carry higher preheat than the non-weathering grades.
Understanding the FC Preheat for M270M Gr.345W / M270 Gr.50W
Weathering 345 MPa (50 ksi) bridge steel for unpainted service. Under D1.5 fracture-critical requirements (Clause 12), the combination of H8 hydrogen designation and this heat input band requires 275°F minimum preheat at 40–60 mm (1½–2½ in). Lower hydrogen levels (H4 < H8 < H16) allow lower preheat because less hydrogen enters the weld deposit. Similarly, higher heat input reduces preheat requirements because slower cooling rates give hydrogen more time to diffuse out.
Where M270M Gr.345W / M270 Gr.50W Is Used
Deployed in unpainted bridge plate girders across humid, coastal, and high-maintenance-cost environments. The weathering patina eliminates lifetime repainting cycles estimated at $15–25/sq ft per cycle. Weld filler must match the weathering composition (E8018-W2 or ER80S-G-W) for exposed joints to ensure the weld face develops the same protective oxide as the base metal. Conventional Gr.345W is being replaced by HPS345W in new designs due to superior weldability.
H8 Hydrogen Control for M270M Gr.345W / M270 Gr.50W
Weathering Gr.345W (50W) with H8 represents the standard practice for most unpainted bridge fabrication. Gas-shielded FCAW wires commonly achieve H8 designation, making this the natural hydrogen level for high-productivity shop welding on weathering grade plate girders.
Why Preheat Matters at 40–60 mm (1½–2½ in)
Material from 40 to 65 mm (1-1/2 to 2-1/2 in) covers heavy girder flanges, thick splice plates, and main member plate. This is the critical thickness range for bridge fabrication — preheat reaches 65°C (150°F) for Group 1 and 80°C (175°F) for Group 2. FC preheat at this thickness can exceed 200°C (400°F) depending on hydrogen level and heat input.
M270M Gr.345W / M270 Gr.50W at 40–60 mm (1½–2½ in)
Gr.345W (50W) at 40–65 mm covers girder flanges on medium-span unpainted bridges where the lifecycle cost of eliminating repainting outweighs the modest material premium. The higher-alloy chemistry for weathering resistance increases the carbon equivalent compared to plain Gr.345, which is why D1.5 assigns weathering grades to Tables 12.6/12.7 rather than 12.4/12.5 for FC preheat — a separate set of tables with generally higher preheat requirements reflecting the increased cracking susceptibility of the Cu-Cr-Ni alloying elements. Flange splice procedures must account for the weathering composition by matching filler metals to ensure consistent patina development across the weld face.
Other Bridge Steels at H8 > 2.8 kJ/mm · 40–60 mm (1½–2½ in)
| Steel | Table | Preheat |
|---|---|---|
| M270M Gr.250 / M270 Gr.36 | A | 175°F (80°C) |
| M270M Gr.345 / M270 Gr.50 | A | 175°F (80°C) |
| M270M Gr.345S / M270 Gr.50S | A | 175°F (80°C) |
| M270M HPS345W / M270 HPS50W | B | 275°F (140°C) |
M270M Gr.345W / M270 Gr.50W at H8 > 2.8 kJ/mm
Try Different Combinations
Use the D1.5 Bridge Preheat Calculator to look up any AASHTO M270 steel, hydrogen level, and heat input combination. Also see the D1.1 Preheat Calculator for structural steel.
Related Guides
For fracture-critical M270M Gr.345W / M270 Gr.50W welded with H8-designated consumables at 40–60 mm (1½–2½ in) thickness and > 2.8 kJ/mm heat input, the minimum preheat is 275°F (140°C) per D1.5 Table 12.6/12.7.
Non-fracture-critical (Table 6.3) preheat is a simple thickness-based lookup. Fracture-critical (Tables 12.4–12.8) adds hydrogen level and heat input as variables, typically requiring higher preheat. For FC members, the hydrogen designator on the consumable classification directly determines the minimum preheat.
Higher heat input means slower cooling rates, giving hydrogen more time to diffuse out of the weld zone. At > 2.8 kJ/mm, the 275°F preheat balances the hydrogen level and cooling rate. Moving to a higher heat input band would typically reduce the required preheat for the same hydrogen level and thickness.
For non-fracture-critical: 65°C (150°F) for Group 1 grades, 80°C (175°F) for Group 2. For fracture-critical: consult Tables 12.4–12.8 based on the specific steel grade, hydrogen designator, and heat input. FC preheat at this thickness is typically 90–200°C (200–400°F) depending on those variables.
D1.5:2025 reference data. Not affiliated with AWS or AASHTO.