Ön Isıtma M270M HPS690W — 2.0–2.8 kJ/mm, 20–25 mm: 250–400°F

M270M HPS690W / M270 HPS100W

AASHTO M270M HPS690W (M270 HPS100W) is the highest-strength bridge steel at 690 MPa (100 ksi) yield, reserved for the most demanding long-span and cable-stayed bridge applications. It follows a completely different FC preheat table (Table 12.8) with min-max ranges and many prohibited thickness-heat input combinations marked with “—”. Table 12.8 requires H4 or H8 designated consumables; H16 is not permitted. NFC preheat per Table 6.3 Group 2; maximum interpass per Table 6.4 is 205°C (400°F) for material up to 40 mm, 230°C (450°F) above.

M270M HPS690W / M270 HPS100W Nerede Kullanılır

Reserved for the most demanding long-span and cable-stayed bridge applications where maximum weight reduction justifies the material cost premium and fabrication complexity. Table 12.8 imposes both minimum AND maximum preheat limits, and many thickness-heat input combinations are outright prohibited. Fabricators must plan weld procedures around the permitted combinations before cutting plate. Filler metals must carry the H4 or H8 supplemental designator — H16 is not permitted for HPS690W FC applications.

20–25 mm (3/4–1 in)'de M270M HPS690W / M270 HPS100W

At 20–40 mm, HPS690W (HPS100W) appears in cable-stayed bridge edge girder flanges and heavily loaded truss members. The preheat range requirement (both min and max) becomes more restrictive — the window between required minimum and maximum narrows as thickness increases, leaving less margin for production variation. Fabricators must plan weld sequences to maintain temperature within the narrow permitted band throughout multi-pass welds.

M270M HPS690W / M270 HPS100W için Min–Maks Ön Isıtma Kontrolü

Highest-strength 690 MPa (100 ksi) bridge steel with restricted FC combinations. Table 12.8 specifies a preheat RANGE of 250–400°F for this thickness and heat input combination. Unlike other FC grades, HPS690W requires both minimum AND maximum preheat control because the Q&T microstructure is sensitive to both excessive and insufficient heat. Many thickness-heat input combinations are prohibited ("—" in the table) because no safe preheat window exists — the steel cannot be reliably welded under those conditions.

2.0–2.8 kJ/mm'de M270M HPS690W / M270 HPS100W

Farklı Kombinasyonları Dene

Herhangi bir AASHTO M270 çelik, hidrojen seviyesi ve ısı girdisi kombinasyonunu aramak için D1.5 Köprü Ön Isıtma Hesap Makinesini kullanın. Yapısal çelik için D1.1 Ön Isıtma Hesap Makinesine de bakın.

İlgili Kılavuzlar