Ön Isıtma M270M Gr.345W — H8, Mid HI, 40–60 mm: 300°F

M270M Gr.345W / M270 Gr.50W

AASHTO M270M Gr.345W (M270 Gr.50W) is a weathering bridge steel with 345 MPa (50 ksi) yield that forms a protective oxide patina for unpainted bridge service. The copper-chromium-nickel alloying provides atmospheric corrosion resistance, eliminating lifetime repainting costs estimated at $15–25 per square foot per cycle. Weld filler must match the weathering composition (E8018-W2 or equivalent) for exposed joints. NFC preheat per Table 6.3 Group 1; FC per Tables 12.6/12.7 which carry higher preheat than the non-weathering grades.

M270M Gr.345W / M270 Gr.50W için FC Ön Isıtmayı Anlama

Weathering 345 MPa (50 ksi) bridge steel for unpainted service. Under D1.5 fracture-critical requirements (Clause 12), the combination of H8 hydrogen designation and this heat input band requires 300°F minimum preheat at 40–60 mm (1½–2½ in). Lower hydrogen levels (H4 < H8 < H16) allow lower preheat because less hydrogen enters the weld deposit. Similarly, higher heat input reduces preheat requirements because slower cooling rates give hydrogen more time to diffuse out.

M270M Gr.345W / M270 Gr.50W Nerede Kullanılır

Deployed in unpainted bridge plate girders across humid, coastal, and high-maintenance-cost environments. The weathering patina eliminates lifetime repainting cycles estimated at $15–25/sq ft per cycle. Weld filler must match the weathering composition (E8018-W2 or ER80S-G-W) for exposed joints to ensure the weld face develops the same protective oxide as the base metal. Conventional Gr.345W is being replaced by HPS345W in new designs due to superior weldability.

M270M Gr.345W / M270 Gr.50W için H8 Hidrojen Kontrolü

Weathering Gr.345W (50W) with H8 represents the standard practice for most unpainted bridge fabrication. Gas-shielded FCAW wires commonly achieve H8 designation, making this the natural hydrogen level for high-productivity shop welding on weathering grade plate girders.

40–60 mm (1½–2½ in)'de Ön Isıtma Neden Önemlidir

Material from 40 to 65 mm (1-1/2 to 2-1/2 in) covers heavy girder flanges, thick splice plates, and main member plate. This is the critical thickness range for bridge fabrication — preheat reaches 65°C (150°F) for Group 1 and 80°C (175°F) for Group 2. FC preheat at this thickness can exceed 200°C (400°F) depending on hydrogen level and heat input.

40–60 mm (1½–2½ in)'de M270M Gr.345W / M270 Gr.50W

Gr.345W (50W) at 40–65 mm covers girder flanges on medium-span unpainted bridges where the lifecycle cost of eliminating repainting outweighs the modest material premium. The higher-alloy chemistry for weathering resistance increases the carbon equivalent compared to plain Gr.345, which is why D1.5 assigns weathering grades to Tables 12.6/12.7 rather than 12.4/12.5 for FC preheat — a separate set of tables with generally higher preheat requirements reflecting the increased cracking susceptibility of the Cu-Cr-Ni alloying elements. Flange splice procedures must account for the weathering composition by matching filler metals to ensure consistent patina development across the weld face.

H8 2.0–2.8 kJ/mm · 40–60 mm (1½–2½ in)'de Diğer Köprü Çelikleri

H8 2.0–2.8 kJ/mm'de M270M Gr.345W / M270 Gr.50W

Farklı Kombinasyonları Dene

Herhangi bir AASHTO M270 çelik, hidrojen seviyesi ve ısı girdisi kombinasyonunu aramak için D1.5 Köprü Ön Isıtma Hesap Makinesini kullanın. Yapısal çelik için D1.1 Ön Isıtma Hesap Makinesine de bakın.

İlgili Kılavuzlar