예열 M270M Gr.345S — H16, Mid HI, 20–40 mm: 175°F

M270M Gr.345S / M270 Gr.50S

AASHTO M270M Gr.345S (M270 Gr.50S) is the structural shape variant of Gr.345, intended for rolled W-shapes and channels used in bridge framing. The "S" suffix indicates the shape-specific chemistry and mechanical property requirements. Used in cross-frame angles, diaphragm members, and built-up sections where rolled shapes are specified rather than plate. Preheat requirements match Gr.345 — Table 6.3 Group 1 for NFC, Tables 12.4/12.5 for FC applications.

M270M Gr.345S / M270 Gr.50S의 FC 예열 이해

Shape-grade 345 MPa (50 ksi) steel for rolled bridge members. Under D1.5 fracture-critical requirements (Clause 12), the combination of H16 hydrogen designation and this heat input band requires 175°F minimum preheat at 20–40 mm (3/4–1½ in). Lower hydrogen levels (H4 < H8 < H16) allow lower preheat because less hydrogen enters the weld deposit. Similarly, higher heat input reduces preheat requirements because slower cooling rates give hydrogen more time to diffuse out.

M270M Gr.345S / M270 Gr.50S이 사용되는 곳

Used as rolled W-shapes and channels in bridge cross-frames, diaphragm members, and built-up sections. The "S" shape designation indicates procurement under AASHTO M270 with shape-specific chemistry and mandatory CVN testing. Common applications include WT sections for cross-frame members, MC channels for diaphragms, and W-shapes for floor beams on shorter spans. Weld details are primarily fillet welds at gusset connections and clip angles.

M270M Gr.345S / M270 Gr.50S의 H16 수소 제어

Gr.345S (50S) at H16 applies primarily to field-erected cross-frame connections using self-shielded FCAW. The higher preheat requirement at H16 can be challenging to maintain on thin shape flanges that lose heat rapidly to the surrounding air — electric resistance heating pads help maintain uniform temperature.

20–40 mm (3/4–1½ in)에서 예열이 중요한 이유

Material from 20 to 40 mm (3/4 to 1-1/2 in) includes many girder web plates, splice plates, and bearing stiffener plates. Preheat increases to 20°C (70°F) for Group 1 and 50°C (125°F) for Group 2 under Table 6.3. The thicker section slows hydrogen diffusion, requiring higher preheat to maintain safe cooling rates.

20–40 mm (3/4–1½ in)에서의 M270M Gr.345S / M270 Gr.50S

At 20–40 mm flange thickness, Gr.345S (50S) W-shapes serve as floor beams on shorter spans and as bracing members in steel box girders. Connection details include moment connections to girder webs requiring CJP flange welds with backing bars. Preheat is applied to the thicker element at the connection — when a 25 mm shape connects to a 50 mm plate, preheat must meet the requirement for the 50 mm thickness tier.

H16 지정 시 높은 예열

H16 용접재료는 100g당 최대 16 mL의 확산성 수소를 허용합니다 — FC 교량 용접에서 허용되는 가장 높은 수준입니다. 20–40 mm (3/4–1½ in)에서 2.0–2.8 kJ/mm 입열량 시 175°F (80°C) 예열은 높은 수소 잠재력을 보상합니다.

H16 2.0–2.8 kJ/mm · 20–40 mm (3/4–1½ in)에서의 다른 교량 강재

H16 2.0–2.8 kJ/mm에서의 M270M Gr.345S / M270 Gr.50S

다양한 조합 시도

D1.5 교량 예열 계산기를 사용하여 AASHTO M270 강재, 수소 수준 및 입열량 조합을 조회하세요. D1.1 예열 계산기도 참조하세요.