예열 M270M Gr.345 — H16, Low HI, 40–60 mm: 250°F

M270M Gr.345 / M270 Gr.50

AASHTO M270M Gr.345 (M270 Gr.50) is the standard bridge plate and shape grade with 345 MPa (50 ksi) minimum yield, corresponding to ASTM A709 Gr.50. It is the baseline strength for modern highway bridge design per AASHTO LRFD. Used for plate girder flanges, webs, floor beams, cross-frames, and splice plates. Flanges on large plate girders routinely reach 50–75 mm (2–3 in) thick, making preheat compliance at upper thickness tiers a significant production consideration. NFC preheat per Table 6.3 Group 1; FC per Tables 12.4/12.5.

M270M Gr.345 / M270 Gr.50의 FC 예열 이해

Standard 345 MPa (50 ksi) bridge plate for girders and floor beams. Under D1.5 fracture-critical requirements (Clause 12), the combination of H16 hydrogen designation and this heat input band requires 250°F minimum preheat at 40–60 mm (1½–2½ in). Lower hydrogen levels (H4 < H8 < H16) allow lower preheat because less hydrogen enters the weld deposit. Similarly, higher heat input reduces preheat requirements because slower cooling rates give hydrogen more time to diffuse out.

M270M Gr.345 / M270 Gr.50이 사용되는 곳

Standard for highway bridge plate girder flanges, box girder webs, cross-frame angles, bearing sole plates, and splice plates in bolted-welded connections. Gr.345 (50) is the baseline strength for modern AASHTO LRFD bridge design. Flange butt splices, web-to-flange continuous fillet welds, and bearing stiffener clips are the dominant weld types in girder fabrication. Girder flanges typically range from 20 to 75 mm (3/4 to 3 in) thick with widths from 300 to 750 mm (12 to 30 in), requiring extended preheat soak times on thicker flange splices.

M270M Gr.345 / M270 Gr.50의 H16 수소 제어

Gr.345 (50) at H16 requires the highest FC preheat in the standard grade range. The elevated preheat compensates for the substantial hydrogen potential but adds significant production cost on thick girder flanges. Most fabricators avoid H16 for shop work, reserving it only for field processes where lower-hydrogen alternatives are not feasible.

40–60 mm (1½–2½ in)에서 예열이 중요한 이유

Material from 40 to 65 mm (1-1/2 to 2-1/2 in) covers heavy girder flanges, thick splice plates, and main member plate. This is the critical thickness range for bridge fabrication — preheat reaches 65°C (150°F) for Group 1 and 80°C (175°F) for Group 2. FC preheat at this thickness can exceed 200°C (400°F) depending on hydrogen level and heat input.

40–60 mm (1½–2½ in)에서의 M270M Gr.345 / M270 Gr.50

Gr.345 (50) at 40–65 mm includes the main flange plates on medium-span highway bridges. Flange width typically runs 400–600 mm (16–24 in), requiring multi-pass CJP butt splices that accumulate 40–60 passes. Interpass temperature must stay above preheat minimum between passes and below the Table 6.4 maximum — this dual constraint makes temperature monitoring continuous during flange splice welding. Magnetic particle examination of each completed splice adds to the production schedule.

H16 지정 시 높은 예열

H16 용접재료는 100g당 최대 16 mL의 확산성 수소를 허용합니다 — FC 교량 용접에서 허용되는 가장 높은 수준입니다. 40–60 mm (1½–2½ in)에서 1.2–2.0 kJ/mm 입열량 시 250°F (120°C) 예열은 높은 수소 잠재력을 보상합니다.

H16 1.2–2.0 kJ/mm · 40–60 mm (1½–2½ in)에서의 다른 교량 강재

H16 1.2–2.0 kJ/mm에서의 M270M Gr.345 / M270 Gr.50

다양한 조합 시도

D1.5 교량 예열 계산기를 사용하여 AASHTO M270 강재, 수소 수준 및 입열량 조합을 조회하세요. D1.1 예열 계산기도 참조하세요.