예열 M270M Gr.250 — H4, High HI, ≤ 20 mm: 100°F

M270M Gr.250 / M270 Gr.36

AASHTO M270M Gr.250 (M270 Gr.36) is the metric/US customary designation for the basic structural bridge steel with 250 MPa (36 ksi) minimum yield. It is the direct bridge equivalent of ASTM A709 Gr.36, procured under AASHTO M270 with mandatory Charpy V-notch testing per temperature zone. Used for secondary bridge members — lateral bracing, diaphragm plates, floor beam stiffeners, and bearing components where Gr.345 strength is not needed. Non-fracture-critical preheat follows Table 6.3 Group 1; fracture-critical follows Tables 12.4/12.5 with hydrogen and heat input as additional variables.

M270M Gr.250 / M270 Gr.36의 FC 예열 이해

Basic 250 MPa (36 ksi) bridge steel for secondary members. Under D1.5 fracture-critical requirements (Clause 12), the combination of H4 hydrogen designation and this heat input band requires 100°F minimum preheat at ≤ 20 mm (3/4 in). Lower hydrogen levels (H4 < H8 < H16) allow lower preheat because less hydrogen enters the weld deposit. Similarly, higher heat input reduces preheat requirements because slower cooling rates give hydrogen more time to diffuse out.

M270M Gr.250 / M270 Gr.36이 사용되는 곳

Specified for secondary bridge members under AASHTO LRFD — lateral bracing angles, diaphragm plates, floor beam stiffeners, bearing seat components, and railing posts. Gr.250 (36) requires CVN testing per AASHTO temperature zone, distinguishing it from plain ASTM A36 by guaranteeing fracture resistance at the bridge design service temperature. Transverse stiffener fillet welds and floor beam web-to-flange joints are high-frequency fabrication details. Temperature zones (1 through 3) determine CVN test temperature: Zone 1 at 21°C (70°F) for moderate climates, Zone 2 at 4°C (40°F) for cold, Zone 3 at -12°C (10°F) for severe cold.

M270M Gr.250 / M270 Gr.36의 H4 수소 제어

For Gr.250 (36), the H4 restriction to 4 mL/100g diffusible hydrogen provides the widest margin against cold cracking in secondary bridge members. The low carbon equivalent of Gr.250 already makes it one of the least crack-sensitive bridge steels, so the practical benefit of H4 over H8 is primarily preheat reduction — often 10–20°C (20–40°F) lower, which speeds production on high-volume stiffener and bracing fabrication.

≤ 20 mm (3/4 in)에서 예열이 중요한 이유

Material up to 20 mm (3/4 in) covers most cross-frame angles, stiffener clips, lateral bracing members, and light bridge plate. At this thickness, hydrogen diffusion is efficient and preheat requirements are the lowest in Table 6.3 — 10°C (50°F) for both groups. In FC service, this thickness tier also carries the lowest preheat in Tables 12.4–12.7, starting at 40°C (100°F) for H4 consumables.

≤ 20 mm (3/4 in)에서의 M270M Gr.250 / M270 Gr.36

Gr.250 (36) at up to 20 mm is the lightest bridge fabrication scenario — cross-frame angles, stiffener clips, and lateral bracing gussets. Hydrogen diffusion through this thin section is rapid, so preheat has the least influence on cracking resistance. Most fabricators use E7018 SMAW for short fillet welds at this thickness because the joint lengths are too short for mechanized FCAW setup to be economical. Interpass monitoring is minimal at this tier because heat builds slowly in thin plate.

FC 교량 용접용 H4 인증 용접재료

H4 보조 지정은 용접재료가 용착 금속 100g당 최대 4 mL의 확산성 수소를 방출함을 인증합니다. 파괴 임계 M270M Gr.250 / M270 Gr.36에서 ≤ 20 mm (3/4 in) 두께, > 2.8 kJ/mm 입열량 시 H4 용접재료는 FC 표에서 가장 낮은 예열 100°F (40°C)를 달성합니다.

H4 > 2.8 kJ/mm · ≤ 20 mm (3/4 in)에서의 다른 교량 강재

H4 > 2.8 kJ/mm에서의 M270M Gr.250 / M270 Gr.36

다양한 조합 시도

D1.5 교량 예열 계산기를 사용하여 AASHTO M270 강재, 수소 수준 및 입열량 조합을 조회하세요. D1.1 예열 계산기도 참조하세요.