M270M Gr.345W予熱 — H16、Mid HI、≤ 20 mm: 125°F

M270M Gr.345W / M270 Gr.50W

AASHTO M270M Gr.345W (M270 Gr.50W) is a weathering bridge steel with 345 MPa (50 ksi) yield that forms a protective oxide patina for unpainted bridge service. The copper-chromium-nickel alloying provides atmospheric corrosion resistance, eliminating lifetime repainting costs estimated at $15–25 per square foot per cycle. Weld filler must match the weathering composition (E8018-W2 or equivalent) for exposed joints. NFC preheat per Table 6.3 Group 1; FC per Tables 12.6/12.7 which carry higher preheat than the non-weathering grades.

M270M Gr.345W / M270 Gr.50WのFC予熱を理解する

Weathering 345 MPa (50 ksi) bridge steel for unpainted service. Under D1.5 fracture-critical requirements (Clause 12), the combination of H16 hydrogen designation and this heat input band requires 125°F minimum preheat at ≤ 20 mm (3/4 in). Lower hydrogen levels (H4 < H8 < H16) allow lower preheat because less hydrogen enters the weld deposit. Similarly, higher heat input reduces preheat requirements because slower cooling rates give hydrogen more time to diffuse out.

M270M Gr.345W / M270 Gr.50Wの使用箇所

Deployed in unpainted bridge plate girders across humid, coastal, and high-maintenance-cost environments. The weathering patina eliminates lifetime repainting cycles estimated at $15–25/sq ft per cycle. Weld filler must match the weathering composition (E8018-W2 or ER80S-G-W) for exposed joints to ensure the weld face develops the same protective oxide as the base metal. Conventional Gr.345W is being replaced by HPS345W in new designs due to superior weldability.

M270M Gr.345W / M270 Gr.50WにおけるH16水素管理

Weathering Gr.345W (50W) at H16 is used for field splices when self-shielded FCAW is the only practical process due to wind exposure on elevated bridge erection. The significantly higher preheat at H16 — often 40–60°F above H4 — makes weather-window scheduling critical for winter field splice operations.

≤ 20 mm (3/4 in)で予熱が重要な理由

Material up to 20 mm (3/4 in) covers most cross-frame angles, stiffener clips, lateral bracing members, and light bridge plate. At this thickness, hydrogen diffusion is efficient and preheat requirements are the lowest in Table 6.3 — 10°C (50°F) for both groups. In FC service, this thickness tier also carries the lowest preheat in Tables 12.4–12.7, starting at 40°C (100°F) for H4 consumables.

≤ 20 mm (3/4 in)でのM270M Gr.345W / M270 Gr.50W

Gr.345W (50W) weathering steel at thin plate thickness appears in unpainted bridge bearing stiffeners and web attachment plates exposed to the atmosphere. Filler metal must match the weathering composition — E8018-W2 for SMAW or ER80S-G-W for GMAW. The patina development on thin plate is rapid (6–18 months) but requires proper drainage detailing to prevent pack rust between closely spaced plates.

H16指定での高い予熱

H16溶接材料は100gあたり最大16mLの拡散性水素を許容します — 橋梁FC溶接で許可される最高レベルです。2.0–2.8 kJ/mm入熱での≤ 20 mm (3/4 in)では、125°F (50°C)予熱が高い水素ポテンシャルを補います。この継手にH8またはH4溶接材料に切り替えると必要な予熱が低下します。

H16 2.0–2.8 kJ/mm · ≤ 20 mm (3/4 in)における他の橋梁鋼材

H16 2.0–2.8 kJ/mmでのM270M Gr.345W / M270 Gr.50W

別の組み合わせを試す

D1.5橋梁予熱計算機を使用して、AASHTO M270鋼材の水素レベルと入熱の任意の組み合わせを検索できます。構造用鋼にはD1.1予熱計算機もご覧ください。