M270M Gr.345S予熱 — H16、Low HI、20–40 mm: 200°F

M270M Gr.345S / M270 Gr.50S

AASHTO M270M Gr.345S (M270 Gr.50S) is the structural shape variant of Gr.345, intended for rolled W-shapes and channels used in bridge framing. The "S" suffix indicates the shape-specific chemistry and mechanical property requirements. Used in cross-frame angles, diaphragm members, and built-up sections where rolled shapes are specified rather than plate. Preheat requirements match Gr.345 — Table 6.3 Group 1 for NFC, Tables 12.4/12.5 for FC applications.

M270M Gr.345S / M270 Gr.50SのFC予熱を理解する

Shape-grade 345 MPa (50 ksi) steel for rolled bridge members. Under D1.5 fracture-critical requirements (Clause 12), the combination of H16 hydrogen designation and this heat input band requires 200°F minimum preheat at 20–40 mm (3/4–1½ in). Lower hydrogen levels (H4 < H8 < H16) allow lower preheat because less hydrogen enters the weld deposit. Similarly, higher heat input reduces preheat requirements because slower cooling rates give hydrogen more time to diffuse out.

M270M Gr.345S / M270 Gr.50Sの使用箇所

Used as rolled W-shapes and channels in bridge cross-frames, diaphragm members, and built-up sections. The "S" shape designation indicates procurement under AASHTO M270 with shape-specific chemistry and mandatory CVN testing. Common applications include WT sections for cross-frame members, MC channels for diaphragms, and W-shapes for floor beams on shorter spans. Weld details are primarily fillet welds at gusset connections and clip angles.

M270M Gr.345S / M270 Gr.50SにおけるH16水素管理

Gr.345S (50S) at H16 applies primarily to field-erected cross-frame connections using self-shielded FCAW. The higher preheat requirement at H16 can be challenging to maintain on thin shape flanges that lose heat rapidly to the surrounding air — electric resistance heating pads help maintain uniform temperature.

20–40 mm (3/4–1½ in)で予熱が重要な理由

Material from 20 to 40 mm (3/4 to 1-1/2 in) includes many girder web plates, splice plates, and bearing stiffener plates. Preheat increases to 20°C (70°F) for Group 1 and 50°C (125°F) for Group 2 under Table 6.3. The thicker section slows hydrogen diffusion, requiring higher preheat to maintain safe cooling rates.

20–40 mm (3/4–1½ in)でのM270M Gr.345S / M270 Gr.50S

At 20–40 mm flange thickness, Gr.345S (50S) W-shapes serve as floor beams on shorter spans and as bracing members in steel box girders. Connection details include moment connections to girder webs requiring CJP flange welds with backing bars. Preheat is applied to the thicker element at the connection — when a 25 mm shape connects to a 50 mm plate, preheat must meet the requirement for the 50 mm thickness tier.

H16指定での高い予熱

H16溶接材料は100gあたり最大16mLの拡散性水素を許容します — 橋梁FC溶接で許可される最高レベルです。1.2–2.0 kJ/mm入熱での20–40 mm (3/4–1½ in)では、200°F (100°C)予熱が高い水素ポテンシャルを補います。この継手にH8またはH4溶接材料に切り替えると必要な予熱が低下します。

H16 1.2–2.0 kJ/mm · 20–40 mm (3/4–1½ in)における他の橋梁鋼材

H16 1.2–2.0 kJ/mmでのM270M Gr.345S / M270 Gr.50S

別の組み合わせを試す

D1.5橋梁予熱計算機を使用して、AASHTO M270鋼材の水素レベルと入熱の任意の組み合わせを検索できます。構造用鋼にはD1.1予熱計算機もご覧ください。