التسخين المسبق M270M HPS485W — H16، Low HI، 20–40 mm: 250°F

M270M HPS485W / M270 HPS70W

AASHTO M270M HPS485W (M270 HPS70W) is a high-performance weathering steel with 485 MPa (70 ksi) yield, used in long-span bridge girder flanges and heavily loaded members where weight reduction is critical. Produced as quenched-and-tempered plate up to 100 mm (4 in) thick. The high strength level places it in NFC Group 2 (Table 6.3) with higher minimum preheat than Group 1. FC preheat follows Tables 12.6/12.7 alongside the 345W grades but at higher temperatures reflecting the increased hardenability. Maximum interpass per Table 6.4 is 230°C (450°F) to protect the Q&T microstructure.

فهم التسخين المسبق FC لـ M270M HPS485W / M270 HPS70W

High-performance 485 MPa (70 ksi) weathering bridge steel. Under D1.5 fracture-critical requirements (Clause 12), the combination of H16 hydrogen designation and this heat input band requires 250°F minimum preheat at 20–40 mm (3/4–1½ in). Lower hydrogen levels (H4 < H8 < H16) allow lower preheat because less hydrogen enters the weld deposit. Similarly, higher heat input reduces preheat requirements because slower cooling rates give hydrogen more time to diffuse out.

أين يُستخدم M270M HPS485W / M270 HPS70W

Used in long-span bridge main girder flanges, cable-stayed bridge edge girders, and heavily loaded interchange ramp girders where weight reduction is critical. Enables 20–30% weight savings versus Gr.345 designs, allowing shallower girder sections that reduce embankment costs. Flange thickness often exceeds 50 mm (2 in), making preheat and interpass control critical at every CJP splice. Fabricators must use dual-readout temperature monitoring to ensure joints stay within the qualified range between minimum preheat and maximum interpass.

التحكم في الهيدروجين H16 لـ M270M HPS485W / M270 HPS70W

HPS485W (HPS70W) at H16 represents the highest-risk FC scenario for this grade — the combination of high strength, high hardenability, and high hydrogen demands the maximum preheat in Tables 12.6/12.7. Production scheduling must account for extended preheat soak times at every joint. Many fabricators refuse H16 on HPS485W, requiring H4 or H8 in their shop standards.

لماذا يهم التسخين المسبق عند 20–40 mm (3/4–1½ in)

Material from 20 to 40 mm (3/4 to 1-1/2 in) includes many girder web plates, splice plates, and bearing stiffener plates. Preheat increases to 20°C (70°F) for Group 1 and 50°C (125°F) for Group 2 under Table 6.3. The thicker section slows hydrogen diffusion, requiring higher preheat to maintain safe cooling rates.

M270M HPS485W / M270 HPS70W عند 20–40 mm (3/4–1½ in)

At 20–40 mm, HPS485W (HPS70W) serves as the primary flange material for long-span bridge girders where weight reduction is the design driver. The 70 ksi yield enables 20–30% thinner flanges versus Gr.345 designs, reducing dead load and allowing shallower girder depths that save embankment costs. CJP flange splices at this thickness require precise heat input control to stay within the FC table parameters.

تسخين مسبق أعلى بتصنيف H16

المواد المستهلكة H16 تسمح بحد أقصى 16 مل من الهيدروجين القابل للانتشار لكل 100 غ — أعلى مستوى مسموح به للحام FC للجسور. عند 20–40 mm (3/4–1½ in) بمدخل حراري 1.2–2.0 kJ/mm، التسخين المسبق 250°F (120°C) يعوض عن إمكانية الهيدروجين الأعلى.

فولاذ جسور أخرى عند H16 1.2–2.0 kJ/mm · 20–40 mm (3/4–1½ in)

M270M HPS485W / M270 HPS70W عند H16 1.2–2.0 kJ/mm

جرّب تركيبات مختلفة

استخدم حاسبة التسخين المسبق D1.5 للجسور للبحث عن أي فولاذ AASHTO M270 ومستوى هيدروجين وتركيبة مدخل حراري. انظر أيضاً حاسبة التسخين المسبق D1.1 للفولاذ الإنشائي.