A913 Gr.70 Preheat for SAW — up to 3/4"

SAW (Submerged Arc Welding)

SAW submerges the arc beneath granular flux for highest deposition rates, flat/horizontal only. Category B in Table 5.11.

SAW on high-strength plate selects wire-flux combinations by the steel's Table 5.6 base-metal group, not its Table 5.11 preheat category: Table 5.7 marks AWS A5.17 carbon-steel combinations N/A for Groups III, IV and V and lists AWS A5.23 low-alloy combinations such as F8AX-E(C)XXX-A2 for Group III and F9AX-E(C)XXX-A2 for Group IV. Heat input control is particularly important on TMCP grades because SAW naturally deposits high heat input due to the deeply penetrating arc.

Why SAW for A913 Gr.70 at up to 3/4"

Why SAW for A913 Gr.70 at up to 3/4"? SAW delivers 15-40 lb/hr deposition — the highest deposition rate among available processes. Position capability: flat and horizontal only. Suitability: shop only.

Filler Metal for SAW

Wire: EM12K or EL12 with matching flux (AWS A5.17). Common combo: F7A2-EM12K. Diameter: 3/32" or 7/64". AWS A5.17 Figure 1U uses A for as-welded and P for PWHT, not flux activity. Annex A6.1 defines active versus neutral flux by weld-metal Mn and Si change with arc voltage (Wall Neutrality Number); primary use of neutral fluxes is multipass welding and of active fluxes is single-pass welds. Voltage: 28-34V. Current: 400-800A depending on joint size. Travel: 12-24 ipm.

Typical values for reference — always verify against your approved WPS and electrode manufacturer data.

A913 Gr.70

ASTM A913 Grade 70 (70 ksi yield, 90 ksi minimum tensile) is a TMCP structural shape used in heavily loaded columns and seismic applications requiring higher strength than Gr.50/60/65. It falls under Category C for standard low-hydrogen processes, with preheat requirements reflecting its higher strength level and CE-IIW of approximately 0.42-0.48. With H8-certified consumables, it qualifies for Category F — 32°F up to 2-1/2”, 150°F above. The TMCP QST microstructure provides inherent resistance to hydrogen cracking through its fine-grained bainitic structure, which is why H8 consumables unlock a reduced-preheat path not available for conventional Q&T steels at similar strength. A913 Gr.70 is primarily available in W14 sections ranging from W14x233 through W14x730, with limited W12 and W36 availability.

Why This Preheat for A913 Gr.70 with SAW

TMCP 70 ksi shape with Category F reduced preheat using H8 consumables. The higher strength level of this steel places it in Category C of Table 5.11, which carries elevated preheat requirements compared to Category B grades. At 50°F minimum with SAW, the submerged arc process with granular flux produces controlled hydrogen levels, with flux condition being the primary variable, but the preheat must still ensure the cooling rate stays slow enough to prevent hydrogen-induced cracking in this higher-hardenability material.

Typical Applications for A913 Gr.70

Used in heavily loaded interior columns of super-tall buildings, transfer truss compression chords, mega-brace members in outrigger systems, stadium roof cantilever supports, and seismic collectors in high-rise cores. A913 Gr.70 TMCP shapes enable smaller column sections, freeing usable floor space on every floor of the building. Column splice butt welds at upper stories and moment connection flange welds carry the highest inspection priority. The 70 ksi yield enables using W14x398 where conventional Gr.50 would require W14x550, saving 38% in material weight and 3-4 inches of floor space per column. Erection splices at every 2-3 stories use CJP groove welds with backing bars removed and back-gouged per seismic detailing requirements. The Category F path with H8 consumables (32°F up to 2-1/2", 150°F above) provides a practical alternative to full Category C preheat on these thick-flange column splices.

Why Preheat Matters at up to 3/4"

Thin material sheds heat quickly, allowing hydrogen to escape the HAZ readily — lowest preheat tier in Table 5.11.

Category C Preheat for A913 Gr.70

Category C in Table 5.11 applies to higher-strength steels where the combination of hardenability and residual stress requires elevated preheat. For A913 Gr.70 at up to 3/4", the 50°F minimum preheat slows the weld cooling rate to prevent formation of crack-susceptible martensite in the heat-affected zone. Maintaining interpass temperature at or above this minimum is especially critical for multi-pass welds on restrained joints.

Other Steels with SAW at up to 3/4"

A913 Gr.70 with SAW

Try Different Combinations

Use the interactive preheat calculator to look up any steel, process, and thickness combination from D1.1:2025 Table 5.11.

A913 Gr.70 Welding Guides