A516 Gr.55/60 Preheat for FCAW — up to 3/4"

FCAW (Flux Cored Arc Welding)

FCAW uses tubular flux-cored wire, available gas-shielded (E71T-1) or self-shielded (E71T-8) for field work. Category B in Table 5.11.

For vessel fabrication, FCAW offers a productivity advantage over SMAW on long circumferential and longitudinal seams. Gas-shielded E71T-1 provides consistent bead profile for radiographic quality. Self-shielded wire is generally not approved for ASME pressure service due to higher inclusion content in the weld deposit.

A516 Gr.55/60

ASTM A516 Grades 55 and 60 are carbon steel plates designed for moderate and lower temperature pressure vessel service. Grade 55 (55 ksi tensile, 30 ksi yield) and Grade 60 (60 ksi tensile, 32 ksi yield) are widely used in storage tanks, heat exchangers, and process drums. Chemistry limits (0.24% max carbon for Gr.55, 0.27% max carbon for Gr.60 on thicker plate) and typical carbon equivalent of 0.38-0.44 qualify them for both Category A (non-low-hydrogen) and Category B preheat in Table 5.11. A516 is produced in plate thicknesses from 1/4" through 12". Grades 55 and 60 may be ordered as-rolled, normalized, or stress-relieved depending on the ASME Code requirements for the specific vessel design temperature and thickness.

Why This Preheat for A516 Gr.55/60 with FCAW

Pressure vessel plate for storage tanks and heat exchangers at moderate strength. With low-hydrogen FCAW, this combination falls under Category B rather than Category A, reflecting the lower hydrogen potential of the consumable. The 32°F minimum preheat is lower than what non-low-hydrogen SMAW would require at the same thickness. Low-hydrogen electrodes and inherently low-hydrogen wire processes reduce the driving force for hydrogen-induced cracking in the heat-affected zone.

Typical Applications for A516 Gr.55/60

Specified for atmospheric storage tank shells per API 650, heat exchanger tube sheets, air receiver vessels, condensate drums, deaerator shells, and low-pressure separator vessels. A516 Gr.60 is the workhorse for ASME VIII Division 1 vessels under 650°F design temperature. Shell-to-head circumferential seams and nozzle reinforcement pads are the primary weld details. Plate thicknesses for API 650 tank shells typically range from 5/16" at the top course to 1" or more at the bottom course depending on tank diameter and liquid specific gravity. Vertical seam welds carry the full hydrostatic head and require complete joint penetration with radiographic examination. Tank diameters range from 15 feet for small day tanks to over 300 feet for crude oil terminal storage. Shop-welded vessel shells are rolled from flat plate with longitudinal seams welded first, then circumferential seams joining shell courses together on the vessel rotator.

Why Preheat Matters at up to 3/4"

Thin material sheds heat quickly, allowing hydrogen to escape the HAZ readily — lowest preheat tier in Table 5.11.

Other Steels with FCAW at up to 3/4"

A516 Gr.55/60 with FCAW

Try Different Combinations

Use the interactive preheat calculator to look up any steel, process, and thickness combination from D1.1:2025 Table 5.11.

A516 Gr.55/60 Welding Guides