A709 Gr.36のSMAW (non-low-hydrogen)用予熱 — over 2-1/2"

SMAW (Non-Low-Hydrogen)

Non-low-hydrogen SMAW (E6010/E6011) uses cellulosic electrodes with higher hydrogen potential, assigned to Category A in Table 5.11.

For common structural shapes and plate, non-low-hydrogen SMAW with E6010 or E6011 excels at root passes on open-root groove welds where burn-through control matters. Vertical-up technique with a slight weave keeps the puddle manageable. Rod consumption runs about 10-12 electrodes per pound of weld metal deposited. Electrode stubs should be no shorter than 2 inches to maintain adequate arc length control.

A709 Gr.36

ASTM A709 Grade 36 is the bridge-specific equivalent of A36, used exclusively for highway bridge construction under AASHTO LRFD Bridge Design Specifications. With 36 ksi minimum yield, 58-80 ksi tensile, and mandatory Charpy V-notch testing requirements based on AASHTO temperature zone (Zone 1: 70°F, Zone 2: 40°F, Zone 3: 10°F test temperatures), it qualifies for both Category A and Category B preheat in Table 5.11. Chemistry matches A36 (0.26% max carbon) but the CVN requirements add a fracture resistance guarantee absent from plain A36. A709 Gr.36 is primarily used for secondary bridge members — lateral bracing, floor beam stiffeners, diaphragm plates, and bearing components — where Gr.50 strength is not needed but bridge-code CVN compliance is required.

A709 Gr.36とSMAWでこの予熱が必要な理由

Bridge-specific 36 ksi grade with CVN testing for highway construction. At this thickness, SMAW with non-low-hydrogen electrodes places the joint in Category A of Table 5.11. The minimum preheat of 300°F compensates for the higher diffusible hydrogen from cellulosic electrode coatings. The thicker the material, the longer hydrogen takes to escape the heat-affected zone, which is why preheat rises with thickness even for this common grade.

A709 Gr.36の代表的な適用例

Specified exclusively for highway bridge deck plate, floor beams, lateral bracing, secondary framing, bridge railing posts, abutment bearing stiffeners, and diaphragm plates. A709 Gr.36 requires CVN testing per AASHTO zone classification, distinguishing it from plain A36 by guaranteeing fracture resistance at the bridge’s design service temperature. Transverse stiffener fillet welds and floor beam web-to-flange joints are high-frequency fabrication details in bridge shops. The fracture-critical designation on certain bridge members imposes additional NDT requirements (UT in lieu of RT for CJP welds) and welder qualification testing beyond standard D1.5 provisions. Temperature zones (1 through 3) determine the CVN test temperature for the Charpy specimens: Zone 1 at 70°F for moderate climates, Zone 2 at 40°F for cold climates, and Zone 3 at 10°F for severe cold. Mill certifications must show CVN results meeting the specified zone before plate release to the bridge fabricator.

over 2-1/2"で予熱が重要な理由

The heaviest sections demand the highest preheat in Table 5.11. Multi-pass sequences require maintaining interpass temperature throughout.

SMAW (non-low-hydrogen)とover 2-1/2"における他の鋼材

A709 Gr.36とSMAW (non-low-hydrogen)

別の組み合わせを試す

インタラクティブ予熱計算機を使用して、D1.1:2025 表5.11のあらゆる鋼材・プロセス・板厚の組み合わせを検索できます。

A709 Gr.36溶接ガイド