A106 Gr.BのFCAW用予熱 — over 2-1/2"

FCAW (Flux Cored Arc Welding)

FCAW uses tubular flux-cored wire, available gas-shielded (E71T-1) or self-shielded (E71T-8) for field work. Category B in Table 5.11.

FCAW on pipe butt joints uses gas-shielded wire for root passes with backing rings or ceramic backup. Self-shielded FCAW excels on pipeline tie-in welds in windy field conditions where gas cups cannot maintain a stable envelope. Typical wire diameter for pipe work is 0.045" for root and 0.052" for fill passes.

Why FCAW for A106 Gr.B at over 2-1/2"

Why FCAW for A106 Gr.B at over 2-1/2"? FCAW delivers 8-12 lb/hr deposition — compared to SAW at 15-40 lb/hr. Position capability: all positions. Suitability: field and shop.

Filler Metal for FCAW

Gas-shielded: E71T-1C (AWS A5.20, requires 100% CO2) or E71T-1M (requires 75/25 Ar/CO2 mixed gas) — the C/M suffix designates the required shielding gas. Self-shielded: E71T-8 (no external gas, field-ready). Diameter: 0.045" standard, 1/16" for high-deposition. Stick-out: 3/4" to 1-1/4" (longer than GMAW due to resistive heating of flux core).

Typical values for reference — always verify against your approved WPS and electrode manufacturer data.

A106 Gr.B

ASTM A106 Grade B covers seamless carbon steel pipe for high-temperature service up to about 750°F, with 35 ksi minimum yield and 60 ksi minimum tensile strength. Produced in sizes from 1/4" through 30" NPS, it is the standard pipe material for power plants, refineries, and process piping where elevated temperature and pressure coexist. Chemistry limits (0.30% max carbon, 0.29-1.06% manganese) give it a weldability profile that matches common structural grades with Category A and B preheat requirements. A106 is exclusively seamless, which eliminates the ERW seam concern present in A53. Grade C (40 ksi yield) exists but Grade B handles the vast majority of process piping service.

A106 Gr.BとFCAWでこの予熱が必要な理由

Seamless pipe rated for high-temperature service up to 750°F. With low-hydrogen FCAW, this combination falls under Category B rather than Category A — flux-cored wire in FCAW provides a combination of deoxidizers and low-moisture flux formulations that control hydrogen. The 225°F minimum preheat is lower than what non-low-hydrogen SMAW would require at the same thickness because FCAW significantly reduces the driving force for hydrogen-induced cracking in the heat-affected zone.

A106 Gr.Bの代表的な適用例

Used in boiler steam headers, refinery piping racks, process plant branch connections, heat exchanger nozzle welds, power plant main steam lines, petrochemical reactor feed piping, and high-temperature manifolds. A106 Gr.B butt welds in process piping require joint preparation to B31.1 (power piping) or B31.3 (process piping) depending on service classification. Socket welds on small-bore A106 drain lines and instrument take-offs are common in utility stations, typically 1/2" to 2" NPS. Typical wall thicknesses range from Schedule 40 (0.237" wall on 2" NPS) to Schedule 160 (0.500" wall on 4" NPS) in critical high-energy service. Weld procedure qualification often includes side bend tests and tensile tests specific to the pipe diameter and wall thickness being joined. Field welds at pipe-to-flange connections and valve set-on joints require portable preheating equipment when wall thickness exceeds 1/2".

over 2-1/2"で予熱が重要な理由

The heaviest sections demand the highest preheat in Table 5.11. Multi-pass sequences require maintaining interpass temperature throughout.

FCAWとover 2-1/2"における他の鋼材

A106 Gr.BとFCAW

別の組み合わせを試す

インタラクティブ予熱計算機を使用して、D1.1:2025 表5.11のあらゆる鋼材・プロセス・板厚の組み合わせを検索できます。

A106 Gr.B溶接ガイド