M270M HPS690W予熱 — 1.2–1.6 kJ/mm、13–20 mm: 250–400°F
AASHTO/AWS D1.5:2025（橋梁溶接規格）に基づく、13–20 mm (1/2–3/4 in)板厚におけるM270M HPS690W / M270 HPS100Wの破壊臨界予熱要件。
AWS D1.5:2025に基づく — すべての値は条項に追跡可能。
M270M HPS690W / M270 HPS100W
AASHTO M270M HPS690W (M270 HPS100W) is the highest-strength bridge steel at 690 MPa (100 ksi) yield, reserved for the most demanding long-span and cable-stayed bridge applications. It follows a completely different FC preheat table (Table 12.8) with min-max ranges and many prohibited thickness-heat input combinations marked with “—”. Table 12.8 requires H4 or H8 designated consumables; H16 is not permitted. NFC preheat per Table 6.3 Group 2; maximum interpass per Table 6.4 is 205°C (400°F) for material up to 40 mm, 230°C (450°F) above.
M270M HPS690W / M270 HPS100Wの最低–最高予熱管理
Highest-strength 690 MPa (100 ksi) bridge steel with restricted FC combinations. Table 12.8 specifies a preheat RANGE of 250–400°F for this thickness and heat input combination. Unlike other FC grades, HPS690W requires both minimum AND maximum preheat control because the Q&T microstructure is sensitive to both excessive and insufficient heat. Many thickness-heat input combinations are prohibited ("—" in the table) because no safe preheat window exists — the steel cannot be reliably welded under those conditions.
1.2–1.6 kJ/mmでのM270M HPS690W / M270 HPS100W
別の組み合わせを試す
D1.5橋梁予熱計算機を使用して、AASHTO M270鋼材の水素レベルと入熱の任意の組み合わせを検索できます。構造用鋼にはD1.1予熱計算機もご覧ください。
関連ガイド
D1.5 表12.8は1.2–1.6 kJ/mm入熱での13–20 mm (1/2–3/4 in)におけるHPS690Wに対して250〜400°F (120〜200°C)の予熱範囲を要求します。最低値と最高値の両方を管理する必要があります。
HPS690Wは焼入れと焼戻しによって690 MPa（100 ksi）の強度を実現しています。過剰な予熱は熱影響部の焼戻しされたミクロ組織を軟化させ、鋼材の強度を設計最低値以下に低下させる可能性があります。400°F (200°C)の最高制限がこのQ&T条件を保護します。
D1.5:2025参考データ。AWSおよびAASHTOとの提携なし。