AASHTO/AWS D1.5:2025 · 表12.6/12.7 · 破壊臨界 · H4

M270M HPS345W予熱 — H4、Low HI、≤ 20 mm: 100°F

AASHTO/AWS D1.5:2025（橋梁溶接規格）に基づく、≤ 20 mm (3/4 in)板厚、水素指定H4でのにおけるM270M HPS345W / M270 HPS50Wの破壊臨界予熱要件。

AWS D1.5:2025に基づく — すべての値は条項に追跡可能。

破壊臨界最低予熱・パス間温度

100°F / 40°C

H4水素 · 1.2–2.0 kJ/mm入熱 · ≤ 20 mm (3/4 in)板厚

AASHTO/AWS D1.5M/D1.5:2025 表12.6/12.7

H4指定: AWS A4.3に基づき溶接材料は≤4 mL/100gの拡散性水素を溶着。水素が低いほど予熱要件も低くなります。

参考ツール。プロジェクト適用版およびエンジニア承認済みWPSで確認すること。

AASHTO M270 Standard Grades

M270M HPS345W / M270 HPS50W

AASHTO M270M HPS345W (M270 HPS50W) is a high-performance weathering bridge steel with enhanced weldability through controlled chemistry — 0.11% max carbon, 0.006% max sulfur with calcium treatment for inclusion shape control. Developed under FHWA-funded research to eliminate the lamellar tearing and inconsistent toughness problems of earlier weathering steel bridge designs. The lower carbon equivalent compared to conventional Gr.345W reduces cracking sensitivity at flange splices. NFC preheat per Table 6.3 Group 1; FC per Tables 12.6/12.7.

H4水素管理

橋梁FC溶接用H4認定溶接材料

H4補足記号は、溶接材料が溶着金属100gあたり4mL以下の拡散性水素しか溶着しないことを証明します。1.2–2.0 kJ/mm入熱での≤ 20 mm (3/4 in)板厚における破壊臨界M270M HPS345W / M270 HPS50Wにおいて、H4溶接材料はFCテーブルで最低予熱100°F (40°C)を達成します。予熱低減が優先される場合、これが推奨される水素レベルです。

鋼材比較

H4 1.2–2.0 kJ/mm · ≤ 20 mm (3/4 in)における他の橋梁鋼材

鋼材	表	予熱
M270M Gr.250 / M270 Gr.36	A	100°F (40°C)
M270M Gr.345 / M270 Gr.50	A	100°F (40°C)
M270M Gr.345S / M270 Gr.50S	A	100°F (40°C)
M270M Gr.345W / M270 Gr.50W	B	100°F (40°C)

他の板厚

H4 1.2–2.0 kJ/mmでのM270M HPS345W / M270 HPS50W

インタラクティブ計算機

別の組み合わせを試す

D1.5橋梁予熱計算機を使用して、AASHTO M270鋼材の水素レベルと入熱の任意の組み合わせを検索できます。構造用鋼にはD1.1予熱計算機もご覧ください。

詳細情報