AASHTO/AWS D1.5:2025 · 表12.6/12.7 · 破壊臨界 · H4

M270M Gr.345W予熱 — H4、Low HI、20–40 mm: 200°F

AASHTO/AWS D1.5:2025（橋梁溶接規格）に基づく、20–40 mm (3/4–1½ in)板厚、水素指定H4でのにおけるM270M Gr.345W / M270 Gr.50Wの破壊臨界予熱要件。

AWS D1.5:2025に基づく — すべての値は条項に追跡可能。

破壊臨界最低予熱・パス間温度

200°F / 90°C

H4水素 · 1.2–2.0 kJ/mm入熱 · 20–40 mm (3/4–1½ in)板厚

AASHTO/AWS D1.5M/D1.5:2025 表12.6/12.7

H4指定: AWS A4.3に基づき溶接材料は≤4 mL/100gの拡散性水素を溶着。水素が低いほど予熱要件も低くなります。

参考ツール。プロジェクト適用版およびエンジニア承認済みWPSで確認すること。

AASHTO M270 Standard Grades

M270M Gr.345W / M270 Gr.50W

AASHTO M270M Gr.345W (M270 Gr.50W) is a weathering bridge steel with 345 MPa (50 ksi) yield that forms a protective oxide patina for unpainted bridge service. The copper-chromium-nickel alloying provides atmospheric corrosion resistance, eliminating lifetime repainting costs estimated at $15–25 per square foot per cycle. Weld filler must match the weathering composition (E8018-W2 or equivalent) for exposed joints. NFC preheat per Table 6.3 Group 1; FC per Tables 12.6/12.7 which carry higher preheat than the non-weathering grades.

H4水素管理

橋梁FC溶接用H4認定溶接材料

H4補足記号は、溶接材料が溶着金属100gあたり4mL以下の拡散性水素しか溶着しないことを証明します。1.2–2.0 kJ/mm入熱での20–40 mm (3/4–1½ in)板厚における破壊臨界M270M Gr.345W / M270 Gr.50Wにおいて、H4溶接材料はFCテーブルで最低予熱200°F (90°C)を達成します。予熱低減が優先される場合、これが推奨される水素レベルです。

鋼材比較

H4 1.2–2.0 kJ/mm · 20–40 mm (3/4–1½ in)における他の橋梁鋼材

鋼材	表	予熱
M270M Gr.250 / M270 Gr.36	A	150°F (70°C)
M270M Gr.345 / M270 Gr.50	A	150°F (70°C)
M270M Gr.345S / M270 Gr.50S	A	150°F (70°C)
M270M HPS345W / M270 HPS50W	B	200°F (90°C)

他の板厚

H4 1.2–2.0 kJ/mmでのM270M Gr.345W / M270 Gr.50W

インタラクティブ計算機

別の組み合わせを試す

D1.5橋梁予熱計算機を使用して、AASHTO M270鋼材の水素レベルと入熱の任意の組み合わせを検索できます。構造用鋼にはD1.1予熱計算機もご覧ください。