AASHTO/AWS D1.5:2025 · 表12.4/12.5 · 破壊臨界 · H4

M270M Gr.345S予熱 — H4、Low HI、40–60 mm: 200°F

AASHTO/AWS D1.5:2025（橋梁溶接規格）に基づく、40–60 mm (1½–2½ in)板厚、水素指定H4でのにおけるM270M Gr.345S / M270 Gr.50Sの破壊臨界予熱要件。

AWS D1.5:2025に基づく — すべての値は条項に追跡可能。

破壊臨界最低予熱・パス間温度

200°F / 90°C

H4水素 · 1.2–2.0 kJ/mm入熱 · 40–60 mm (1½–2½ in)板厚

AASHTO/AWS D1.5M/D1.5:2025 表12.4/12.5

H4指定: AWS A4.3に基づき溶接材料は≤4 mL/100gの拡散性水素を溶着。水素が低いほど予熱要件も低くなります。

参考ツール。プロジェクト適用版およびエンジニア承認済みWPSで確認すること。

AASHTO M270 Standard Grades

M270M Gr.345S / M270 Gr.50S

AASHTO M270M Gr.345S (M270 Gr.50S) is the structural shape variant of Gr.345, intended for rolled W-shapes and channels used in bridge framing. The "S" suffix indicates the shape-specific chemistry and mechanical property requirements. Used in cross-frame angles, diaphragm members, and built-up sections where rolled shapes are specified rather than plate. Preheat requirements match Gr.345 — Table 6.3 Group 1 for NFC, Tables 12.4/12.5 for FC applications.

H4水素管理

橋梁FC溶接用H4認定溶接材料

H4補足記号は、溶接材料が溶着金属100gあたり4mL以下の拡散性水素しか溶着しないことを証明します。1.2–2.0 kJ/mm入熱での40–60 mm (1½–2½ in)板厚における破壊臨界M270M Gr.345S / M270 Gr.50Sにおいて、H4溶接材料はFCテーブルで最低予熱200°F (90°C)を達成します。予熱低減が優先される場合、これが推奨される水素レベルです。

鋼材比較

H4 1.2–2.0 kJ/mm · 40–60 mm (1½–2½ in)における他の橋梁鋼材

鋼材	表	予熱
M270M Gr.250 / M270 Gr.36	A	200°F (90°C)
M270M Gr.345W / M270 Gr.50W	B	300°F (150°C)
M270M HPS345W / M270 HPS50W	B	300°F (150°C)
M270M HPS485W / M270 HPS70W	B	300°F (150°C)

他の板厚

H4 1.2–2.0 kJ/mmでのM270M Gr.345S / M270 Gr.50S

インタラクティブ計算機

別の組み合わせを試す

D1.5橋梁予熱計算機を使用して、AASHTO M270鋼材の水素レベルと入熱の任意の組み合わせを検索できます。構造用鋼にはD1.1予熱計算機もご覧ください。