AASHTO/AWS D1.5:2025 · 表12.4/12.5 · 破壊臨界 · H4

M270M Gr.345予熱 — H4、Low HI、20–40 mm: 150°F

AASHTO/AWS D1.5:2025（橋梁溶接規格）に基づく、20–40 mm (3/4–1½ in)板厚、水素指定H4でのにおけるM270M Gr.345 / M270 Gr.50の破壊臨界予熱要件。

AWS D1.5:2025に基づく — すべての値は条項に追跡可能。

破壊臨界最低予熱・パス間温度

150°F / 70°C

H4水素 · 1.2–2.0 kJ/mm入熱 · 20–40 mm (3/4–1½ in)板厚

AASHTO/AWS D1.5M/D1.5:2025 表12.4/12.5

H4指定: AWS A4.3に基づき溶接材料は≤4 mL/100gの拡散性水素を溶着。水素が低いほど予熱要件も低くなります。

参考ツール。プロジェクト適用版およびエンジニア承認済みWPSで確認すること。

AASHTO M270 Standard Grades

M270M Gr.345 / M270 Gr.50

AASHTO M270M Gr.345 (M270 Gr.50) is the standard bridge plate and shape grade with 345 MPa (50 ksi) minimum yield, corresponding to ASTM A709 Gr.50. It is the baseline strength for modern highway bridge design per AASHTO LRFD. Used for plate girder flanges, webs, floor beams, cross-frames, and splice plates. Flanges on large plate girders routinely reach 50–75 mm (2–3 in) thick, making preheat compliance at upper thickness tiers a significant production consideration. NFC preheat per Table 6.3 Group 1; FC per Tables 12.4/12.5.

H4水素管理

橋梁FC溶接用H4認定溶接材料

H4補足記号は、溶接材料が溶着金属100gあたり4mL以下の拡散性水素しか溶着しないことを証明します。1.2–2.0 kJ/mm入熱での20–40 mm (3/4–1½ in)板厚における破壊臨界M270M Gr.345 / M270 Gr.50において、H4溶接材料はFCテーブルで最低予熱150°F (70°C)を達成します。予熱低減が優先される場合、これが推奨される水素レベルです。

鋼材比較

H4 1.2–2.0 kJ/mm · 20–40 mm (3/4–1½ in)における他の橋梁鋼材

鋼材	表	予熱
M270M Gr.250 / M270 Gr.36	A	150°F (70°C)
M270M Gr.345W / M270 Gr.50W	B	200°F (90°C)
M270M HPS345W / M270 HPS50W	B	200°F (90°C)
M270M HPS485W / M270 HPS70W	B	200°F (90°C)

他の板厚

H4 1.2–2.0 kJ/mmでのM270M Gr.345 / M270 Gr.50

インタラクティブ計算機

別の組み合わせを試す

D1.5橋梁予熱計算機を使用して、AASHTO M270鋼材の水素レベルと入熱の任意の組み合わせを検索できます。構造用鋼にはD1.1予熱計算機もご覧ください。

詳細情報