التسخين المسبق M270M Gr.345W — H4، High HI، 20–40 mm: 150°F

M270M Gr.345W / M270 Gr.50W

AASHTO M270M Gr.345W (M270 Gr.50W) is a weathering bridge steel with 345 MPa (50 ksi) yield that forms a protective oxide patina for unpainted bridge service. The copper-chromium-nickel alloying provides atmospheric corrosion resistance, eliminating lifetime repainting costs estimated at $15–25 per square foot per cycle. Weld filler must match the weathering composition (E8018-W2 or equivalent) for exposed joints. NFC preheat per Table 6.3 Group 1; FC per Tables 12.6/12.7 which carry higher preheat than the non-weathering grades.

فهم التسخين المسبق FC لـ M270M Gr.345W / M270 Gr.50W

Weathering 345 MPa (50 ksi) bridge steel for unpainted service. Under D1.5 fracture-critical requirements (Clause 12), the combination of H4 hydrogen designation and this heat input band requires 150°F minimum preheat at 20–40 mm (3/4–1½ in). Lower hydrogen levels (H4 < H8 < H16) allow lower preheat because less hydrogen enters the weld deposit. Similarly, higher heat input reduces preheat requirements because slower cooling rates give hydrogen more time to diffuse out.

أين يُستخدم M270M Gr.345W / M270 Gr.50W

Deployed in unpainted bridge plate girders across humid, coastal, and high-maintenance-cost environments. The weathering patina eliminates lifetime repainting cycles estimated at $15–25/sq ft per cycle. Weld filler must match the weathering composition (E8018-W2 or ER80S-G-W) for exposed joints to ensure the weld face develops the same protective oxide as the base metal. Conventional Gr.345W is being replaced by HPS345W in new designs due to superior weldability.

التحكم في الهيدروجين H4 لـ M270M Gr.345W / M270 Gr.50W

Weathering Gr.345W (50W) with H4 benefits from reduced preheat on field splice joints where maintaining temperature in wind-exposed bridge erection conditions is challenging. The E8018-W2 low-hydrogen electrode commonly used for weathering steel field work typically carries H4 or H8 designation.

لماذا يهم التسخين المسبق عند 20–40 mm (3/4–1½ in)

Material from 20 to 40 mm (3/4 to 1-1/2 in) includes many girder web plates, splice plates, and bearing stiffener plates. Preheat increases to 20°C (70°F) for Group 1 and 50°C (125°F) for Group 2 under Table 6.3. The thicker section slows hydrogen diffusion, requiring higher preheat to maintain safe cooling rates.

M270M Gr.345W / M270 Gr.50W عند 20–40 mm (3/4–1½ in)

At 20–40 mm, Gr.345W (50W) serves as the primary plate for unpainted bridge girder webs and connection plates. Weathering steel butt splices require the same CJP quality as painted Gr.345 but with compositional matching of the filler metal. Improper filler selection leaves a cosmetically distinct weld face that does not develop the same protective oxide, creating a maintenance concern on exposed bridges.

المواد المستهلكة المعتمدة H4 للحام FC للجسور

المؤشر التكميلي H4 يشهد بأن المادة المستهلكة ترسب لا أكثر من 4 مل من الهيدروجين القابل للانتشار لكل 100 غ من المعدن المرسب. للكسر الحرج M270M Gr.345W / M270 Gr.50W عند سماكة 20–40 mm (3/4–1½ in) بمدخل حراري > 2.8 kJ/mm، تحقق مواد H4 أدنى تسخين مسبق 150°F (70°C) في جداول FC.

فولاذ جسور أخرى عند H4 > 2.8 kJ/mm · 20–40 mm (3/4–1½ in)

M270M Gr.345W / M270 Gr.50W عند H4 > 2.8 kJ/mm

جرّب تركيبات مختلفة

استخدم حاسبة التسخين المسبق D1.5 للجسور للبحث عن أي فولاذ AASHTO M270 ومستوى هيدروجين وتركيبة مدخل حراري. انظر أيضاً حاسبة التسخين المسبق D1.1 للفولاذ الإنشائي.