التسخين المسبق M270M Gr.345S — H16، Low HI، > 60 mm: 350°F

M270M Gr.345S / M270 Gr.50S

AASHTO M270M Gr.345S (M270 Gr.50S) is the structural shape variant of Gr.345, intended for rolled W-shapes and channels used in bridge framing. The "S" suffix indicates the shape-specific chemistry and mechanical property requirements. Used in cross-frame angles, diaphragm members, and built-up sections where rolled shapes are specified rather than plate. Preheat requirements match Gr.345 — Table 6.3 Group 1 for NFC, Tables 12.4/12.5 for FC applications.

فهم التسخين المسبق FC لـ M270M Gr.345S / M270 Gr.50S

Shape-grade 345 MPa (50 ksi) steel for rolled bridge members. Under D1.5 fracture-critical requirements (Clause 12), the combination of H16 hydrogen designation and this heat input band requires 350°F minimum preheat at > 60 mm (> 2½ in). Lower hydrogen levels (H4 < H8 < H16) allow lower preheat because less hydrogen enters the weld deposit. Similarly, higher heat input reduces preheat requirements because slower cooling rates give hydrogen more time to diffuse out.

أين يُستخدم M270M Gr.345S / M270 Gr.50S

Used as rolled W-shapes and channels in bridge cross-frames, diaphragm members, and built-up sections. The "S" shape designation indicates procurement under AASHTO M270 with shape-specific chemistry and mandatory CVN testing. Common applications include WT sections for cross-frame members, MC channels for diaphragms, and W-shapes for floor beams on shorter spans. Weld details are primarily fillet welds at gusset connections and clip angles.

التحكم في الهيدروجين H16 لـ M270M Gr.345S / M270 Gr.50S

Gr.345S (50S) at H16 applies primarily to field-erected cross-frame connections using self-shielded FCAW. The higher preheat requirement at H16 can be challenging to maintain on thin shape flanges that lose heat rapidly to the surrounding air — electric resistance heating pads help maintain uniform temperature.

لماذا يهم التسخين المسبق عند > 60 mm (> 2½ in)

Material over 65 mm (2-1/2 in) includes the heaviest bridge girder flanges and box-section walls. Table 6.3 requires 110°C (225°F) for both groups at this thickness. Extended preheat soak time is necessary to achieve uniform through-thickness temperature. FC preheat for the heaviest sections reaches 180–200°C (350–400°F) at the H16 hydrogen level.

M270M Gr.345S / M270 Gr.50S عند > 60 mm (> 2½ in)

Gr.345S (50S) above 65 mm flange thickness is limited to the heaviest jumbo W-shapes (W14×730 or similar) used in critical transfer structures. These sections have significant residual stress from the rolling process that compounds with welding stresses. Full 225°F preheat plus controlled cooling is essential — some fabricators specify post-weld hydrogen release holds at 400°F for 2 hours on jumbo section connections.

تسخين مسبق أعلى بتصنيف H16

المواد المستهلكة H16 تسمح بحد أقصى 16 مل من الهيدروجين القابل للانتشار لكل 100 غ — أعلى مستوى مسموح به للحام FC للجسور. عند > 60 mm (> 2½ in) بمدخل حراري 1.2–2.0 kJ/mm، التسخين المسبق 350°F (180°C) يعوض عن إمكانية الهيدروجين الأعلى.

فولاذ جسور أخرى عند H16 1.2–2.0 kJ/mm · > 60 mm (> 2½ in)

M270M Gr.345S / M270 Gr.50S عند H16 1.2–2.0 kJ/mm

جرّب تركيبات مختلفة

استخدم حاسبة التسخين المسبق D1.5 للجسور للبحث عن أي فولاذ AASHTO M270 ومستوى هيدروجين وتركيبة مدخل حراري. انظر أيضاً حاسبة التسخين المسبق D1.1 للفولاذ الإنشائي.